Features:
E309L-16 provides welding deposit E309-16, but with reduced carbon content(up to 0.04%) to improve resistance to intergranular. E309L-16 type is used to join stainless steel to itself or carbon or low alloy steel. E309L-16 is more suitable than E309-16 for cladding and heat-treated dissimilar joints of carbon or low alloy steel.
-1.0mm and 1.2mm electrodes have strict requirements on welding machine current and need to be adjusted slowly. It is not recommended for beginners and people who are new to welding to use thin plates, especially below 1mm. 1.0mm and 1.2mm electrodes are too thin and not suitable for welding. It will shake back and forth. For customers with rich welding experience, if you want to weld thin plates around 0.5mm, you can choose 1.4mm welding rods. Please check the welding rod current range before welding to avoid unnecessary troubles for both parties.

- Before welding, the electrode needs to be baked at 300-350℃ for 1 hour.
- Try to use DC power supply, and the current should not be too large.


Specifications:
Part name: welding rod
Size: as shown
Standard: GB/T983 E308-16 A5.4 E308-16
Diameter 1.0mm Length 250mm Current 9-22A
Diameter 1.2mm Length 250mm Current 13-32A
Diameter 1.4mm Length 250mm Current 16-40A
Diameter 1.6mm Length 250mm Current 18-50A
Diameter 1.8mm Length 250mm Current 20-55A
Diameter: 2.0mm Length 300mm Current: 30-55A
Diameter: 2.4mm Length 300mm Current: 50-100A
Diameter: 3.2mm Length 350mm Current: 70-130A
Diameter: 4.0mm Length 350mm Current: 100-160A
Material: Stainless steel
Color: As shown


Package Content:
10PCS* Electrode


Note:
1. Please allow 1-3mm difference due to manual measurement, thank you for your understanding!