Resin jewelry Casting With High Wax Content 90% Wax Content Easy To Print Good Casting Effect LCD DLP UV Curing New Models

Model 923-1 is an ash-free casting resin, suitable for standard-thickness rings and some heavy-weight jewelry casting. Containing 30% nano-wax and 60% resin wax, this material features easy burnout (dewaxing). It is specially engineered for direct casting. Its ultra-low viscosity makes it an ideal option for direct casting. Compatible with various DLP/LCD printers with unlocked parameters.
​
​Cleaning solution: 95% Ethanol
​Operating temperature: Room temperature 20~30℃
​Cleaning time: 30 seconds, repeat 3 times
​Equipment: Ultrasonic cleaner
​If an ultrasonic cleaner is not available, immersion cleaning may be used. Each cleaning cycle shall not exceed 1 minute, and three cleaning cycles are recommended. After cleaning, blow off residual cleaning agent on the surface with room-temperature air as soon as possible.
​
​How to Use：
​1. This product is photosensitive. Avoid exposure to sunlight and ultraviolet radiation during storage and handling.
​2. 3D printing resin must be stored in opaque black containers that block ultraviolet radiation.
​3. Sufficient light energy is required to print parts with this product. Therefore, the light intensity of the LED lamp must be inspected regularly.
​4. It is recommended to keep the temperature inside the build chamber between 24℃ and 28℃ during printing. If the temperature is too low or too high while printing, dimensional deviation, inconsistent mechanical properties and printing defects may occur.
​
​Notes:
​- Due to the actual limitations of the printer, printing parameters may vary even for printers of the same model and batch. Objective factors including different wear levels of printer consumables, ambient temperature and humidity, and varying support generation methods may also result in different optimal printing parameters.
​- Verify that your printer and post-curing lamp meet the recommended conditions before use.
​- The information in this document is based on laboratory tests and practical experience. Please note that many factors can affect the mechanical properties and casting quality of the product. Therefore, thorough inspection must be carried out prior to use. This document is for reference only, and we assume no legal liability for the data contained herein.
​- For more information on product hazards and safety, please refer to the MSDS (Material Safety Data Sheet). Contact us if you have any questions.
​- The technical data is subject to change without prior notice. Confirm that this data is the latest revision before use.

The wax content is as high as 90%, easy to print, easy to cast, easy to burn, and has a good casting effect. It can be cleaned with alcohol and is a relatively perfect resin. It is currently the most recommended jewelry casting resin in our store

Curing process: Printing > Cleaning (rinse three times with alcohol or IPA at 95% or higher, no more than 30 seconds per rinse) > Air drying at room temperature > Uniform UV curing for approximately 20~30 minutes

The optimal parameters can only be measured by oneself. Because factors such as printer model, resin model, printing loss, ambient temperature, support strength and density, model placement angle and structure, model projection area, and customer's own printing cost-effectiveness ratio (whether to print efficiency or printing details) all determine the optimal parameters that can only be found by oneself